| * 厂家（产地）： | 沙伯基础 | * 牌号： | C1100HF |
| * 销售方式： | 品牌经销 | 备注说明： | 原厂正牌，货到付款 |
| * 地区： | 全国 |
沙伯基础PC/ABS C1100HF原厂原包，沙伯基础PC/ABS C1100HF货真价实，沙伯基础PC/ABS C1100HF价格优惠，亲！~
专业供应PC+ABS塑胶原料：防火PC+ABS,阻燃PC+ABS，耐高温PC+ABS，耐热PC+ABS，抗冲击PC+ABS，食品级PC+ABS，高冲击PC+ABS，抗紫外线PC+ABS，低粘度PC+ABS，电镀级PC+ABS，加玻纤PC+ABS，耐低温PC+ABS，高流动PC+ABS，无卤PC+ABS，无溴PC+ABS，注塑级PC+ABS，等塑胶原料。
沙伯基础PC/ABS C1100HF物性表
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.12
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR)
|
ISO 1133 | ||
|
260°C/2.16 kg
|
6.00
|
cm³/10min
|
|
|
260°C/5.0 kg
|
20.0
|
cm³/10min
|
|
|
Molding Shrinkage - Flow 2
|
0.50 to 0.70
|
%
|
Internal Method |
|
Water Absorption (Saturation, 23°C)
|
0.60
|
%
|
ISO 62 |
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
0.20
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
2400
|
MPa
|
ISO 527-2/1 |
|
Tensile Stress
|
|||
|
Yield
|
55.0
|
MPa
|
ISO 527-2/5 |
|
Yield
|
55.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Stress
|
|||
|
Break
|
45.0
|
MPa
|
ISO 527-2/5 |
|
Break
|
45.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain
|
|||
|
Yield
|
5.0
|
%
|
ISO 527-2/5 |
|
Yield
|
4.0
|
%
|
ISO 527-2/50 |
|
Tensile Strain
|
|||
|
Break
|
120
|
%
|
ISO 527-2/5 |
|
Break
|
> 50
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 3
|
2300
|
MPa
|
ISO 178 |
|
Flexural Strength 3, 4
|
75.0
|
MPa
|
ISO 178 |
|
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)
|
81.0
|
mg
|
Internal Method |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
|
-30°C 5
|
30
|
kJ/m²
|
|
|
-30°C 6
|
25
|
kJ/m²
|
|
|
23°C 6
|
50
|
kJ/m²
|
|
|
23°C 5
|
55
|
kJ/m²
|
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-30°C 7
|
28
|
kJ/m²
|
|
|
-30°C 8
|
25
|
kJ/m²
|
|
|
23°C 7
|
50
|
kJ/m²
|
|
|
23°C 8
|
50
|
kJ/m²
|
|
|
Unnotched Izod Impact Strength 7
|
ISO 180/1U | ||
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
117
|
|
ISO 2039-2 |
|
Ball Indentation Hardness (H 358/30)
|
99.0
|
MPa
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature 9 (0.45 MPa, Unannealed, 100 mm Span)
|
120
|
°C
|
ISO 75-2/Be |
|
Heat Deflection Temperature 9 (1.8 MPa, Unannealed, 100 mm Span)
|
100
|
°C
|
ISO 75-2/Ae |
|
Vicat Softening Temperature
|
|||
|
--
|
126
|
°C
|
ISO 306/B50 |
|
--
|
128
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test
|
IEC 60695-10-2 | ||
|
75°C
|
Pass
|
|
|
|
115°C 10
|
Pass
|
|
|
|
CLTE - Flow (23 to 60°C)
|
0.000080
|
cm/cm/°C
|
ISO 11359-2 |
|
CLTE - Transverse (23 to 60°C)
|
0.000080
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.20
|
W/m/K
|
ISO 8302 |
|
RTI Elec
|
60.0
|
°C
|
UL 746 |
|
RTI Imp
|
60.0
|
°C
|
UL 746 |
|
RTI Str
|
60.0
|
°C
|
UL 746 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
> 1.0E+15
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
> 1.0E+15
|
ohm·cm
|
IEC 60093 |
|
Electric Strength
|
IEC 60243-1 | ||
|
0.800 mm, in Oil
|
35
|
kV/mm
|
|
|
1.60 mm, in Oil
|
25
|
kV/mm
|
|
|
3.20 mm, in Oil
|
17
|
kV/mm
|
|
|
Relative Permittivity
|
IEC 60250 | ||
|
50 Hz
|
2.80
|
|
|
|
60 Hz
|
2.80
|
|
|
|
1 MHz
|
2.70
|
|
|
|
Dissipation Factor
|
IEC 60250 | ||
|
50 Hz
|
0.0020
|
|
|
|
60 Hz
|
0.0020
|
|
|
|
1 MHz
|
0.0070
|
|
|
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.50 mm
|
HB
|
|
|
|
3.00 mm
|
HB
|
|
|
|
Glow Wire Flammability Index (3.20 mm)
|
650
|
°C
|
IEC 60695-2-12 |