* 厂家(产地): | 美国杜邦 | * 牌号: | 101F-NC010 |
* 销售方式: | 品牌经销 | 备注说明: | 原厂正牌,货到付款 |
* 地区: | 全国 |
美国杜邦PA66,101F-NC010 原厂原包,货真价实,价格优惠,亲!~
本公司长期供应透明尼龙,改性尼龙,食品级尼龙,阻燃尼龙,防火(UL94V0、5VA级)尼龙,耐
磨尼龙,超韧性尼龙,耐寒耐低温尼龙,耐酸碱尼龙,抗紫外线尼龙,防水解尼龙,抗水解尼龙,
增强尼龙,不吸水尼龙,无卤尼龙,热稳定尼龙,弹性尼龙,硬尼龙,挤出尼龙,注塑尼龙,等塑
胶原料。
美国杜邦PA66,101F-NC010 物性表
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Specific Gravity |
1.14
|
--
|
g/cm³
|
ASTM D792 |
Density |
1.14
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage - Flow (3.20 mm) |
1.5
|
--
|
%
|
Internal Method |
Molding Shrinkage | ISO 294-4 | |||
Across Flow: 2.00 mm
|
1.4
|
--
|
%
|
|
Flow: 2.00 mm
|
1.4
|
--
|
%
|
|
Water Absorption (23°C, 24 hr) |
1.2
|
--
|
%
|
ASTM D570 |
Water Absorption (Saturation, 23°C) |
8.5
|
--
|
%
|
ASTM D570 |
Water Absorption (Saturation, 23°C) |
8.5
|
--
|
%
|
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) |
2.6
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C) |
3100
|
1400
|
MPa
|
ISO 527-2 |
Tensile Strength (23°C) |
83.0
|
64.0
|
MPa
|
ASTM D638 |
Tensile Strength (Yield, 23°C) |
83.0
|
--
|
MPa
|
ASTM D638 |
Tensile Stress (Yield, 23°C) |
82.0
|
55.0
|
MPa
|
ISO 527-2 |
Tensile Elongation (Yield, 23°C) |
4.0
|
--
|
%
|
ASTM D638 |
Tensile Strain (Yield, 23°C) |
4.5
|
25
|
%
|
ISO 527-2 |
Tensile Elongation (Break, 23°C) |
50
|
> 300
|
%
|
ASTM D638 |
Tensile Strain (Break, 23°C) |
40
|
> 100
|
%
|
ISO 527-2/50 |
Nominal Tensile Strain at Break (23°C) |
20
|
> 100
|
%
|
ISO 527-2 |
Tensile Creep Modulus (1 hr) |
--
|
1400
|
MPa
|
ISO 899-1 |
Tensile Creep Modulus (1000 hr) |
--
|
930
|
MPa
|
ISO 899-1 |
Flexural Modulus | ASTM D790 | |||
-40°C
|
3200
|
--
|
MPa
|
|
23°C
|
2800
|
1210
|
MPa
|
|
77°C
|
700
|
--
|
MPa
|
|
121°C
|
500
|
--
|
MPa
|
|
Flexural Modulus (23°C) |
2800
|
1200
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength | ISO 179/1eA | |||
-40°C
|
3.0
|
--
|
kJ/m²
|
|
-30°C
|
4.5
|
3.0
|
kJ/m²
|
|
23°C
|
6.0
|
13
|
kJ/m²
|
|
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C
|
400 kJ/m²
|
No Break
|
|
|
23°C
|
No Break
|
No Break
|
|
|
Notched Izod Impact | ASTM D256 | |||
-40°C
|
32
|
--
|
J/m
|
|
23°C
|
53
|
110
|
J/m
|
|
Notched Izod Impact Strength | ISO 180/1A | |||
-40°C
|
5.5
|
--
|
kJ/m²
|
|
-30°C
|
6.0
|
4.0
|
kJ/m²
|
|
23°C
|
5.5
|
11
|
kJ/m²
|
|
Unnotched Izod Impact Strength | ISO 180/1U | |||
-30°C
|
300
|
--
|
kJ/m²
|
|
23°C
|
300 kJ/m²
|
No Break
|
|
|
Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Rockwell Hardness | ASTM D785 | |||
M-Scale
|
71
|
--
|
|
|
R-Scale
|
113
|
--
|
|
|
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Deflection Temperature Under Load (0.45 MPa, Unannealed) |
210
|
--
|
°C
|
ASTM D648 |
Heat Deflection Temperature (0.45 MPa, Unannealed) |
200
|
--
|
°C
|
ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed) |
65.0
|
--
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed) |
70.0
|
--
|
°C
|
ISO 75-2/A |
Brittleness Temperature |
-80.0
|
-65.0
|
°C
|
ASTM D746 |
Glass Transition Temperature |
60.0
|
--
|
°C
|
ISO 11357-2 |
Melting Temperature |
263
|
--
|
°C
|
ASTM D3418 |
Melting Temperature 2 |
262
|
--
|
°C
|
ISO 11357-3 |
CLTE - Flow (23 to 55°C) |
0.00010
|
--
|
cm/cm/°C
|
ASTM E831 |
CLTE - Flow (23 to 55°C) |
0.00010
|
--
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ASTM E831 |
CLTE - Transverse (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Surface Resistivity |
1.0E+14
|
--
|
ohms
|
ASTM D257 |
Surface Resistivity |
1.0E+12
|
1.0E+12
|
ohms
|
IEC 60093 |
Volume Resistivity (23°C) |
1.0E+15
|
--
|
ohm·cm
|
ASTM D257 |
Volume Resistivity |
1.0E+15
|
1.0E+16
|
ohm·cm
|
IEC 60093 |
Dielectric Strength 3 | ASTM D149 | |||
23°C, 1.60 mm
|
23
|
--
|
kV/mm
|
|
23°C, 3.20 mm
|
17
|
--
|
kV/mm
|
|
Dielectric Constant | ASTM D150 | |||
23°C, 100 Hz
|
4.10
|
--
|
|
|
23°C, 1 kHz
|
4.00
|
--
|
|
|
23°C, 1 MHz
|
3.70
|
--
|
|
|
Relative Permittivity | IEC 60250 | |||
23°C, 100 Hz
|
3.80
|
8.00
|
|
|
23°C, 1 kHz
|
3.90
|
7.00
|
|
|
23°C, 1 MHz
|
3.60
|
4.60
|
|
|
Dissipation Factor | ASTM D150 | |||
23°C, 100 Hz
|
0.010
|
--
|
|
|
23°C, 1 kHz
|
0.020
|
--
|
|
|
23°C, 1 MHz
|
0.020
|
--
|
|
|
Dissipation Factor | IEC 60250 | |||
23°C, 100 Hz
|
0.014
|
--
|
|
|
23°C, 1 kHz
|
0.020
|
0.020
|
|
|
23°C, 1 MHz
|
0.018
|
0.10
|
|
|
Electric Strength (23°C, 1.00 mm) |
32
|
26
|
kV/mm
|
IEC 60243-1 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating - UL | UL 94 | |||
0.400 mm
|
V-2
|
--
|
|
|
0.710 mm
|
V-2
|
--
|
|
|
1.50 mm
|
V-2
|
--
|
|
|
3.00 mm
|
V-2
|
--
|
|
|
6.00 mm
|
V-2
|
--
|
|
|
Flammability Classification | IEC 60695-11-10, -20 | |||
0.400 mm
|
V-2
|
--
|
|
|
0.710 mm
|
V-2
|
--
|
|
|
1.50 mm
|
V-2
|
--
|
|
|
3.00 mm
|
V-2
|
--
|
|
|
6.00 mm
|
V-2
|
--
|
|
|
Glow Wire Flammability Index | IEC 60695-2-12 | |||
0.400 mm
|
960
|
--
|
°C
|
|
0.710 mm
|
960
|
--
|
°C
|
|
1.50 mm
|
960
|
--
|
°C
|
|
3.00 mm
|
960
|
--
|
°C
|
|
Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
0.400 mm
|
900
|
--
|
°C
|
|
0.710 mm
|
725
|
--
|
°C
|
|
1.50 mm
|
750
|
--
|
°C
|
|
3.00 mm
|
800
|
--
|
°C
|
|
Oxygen Index |
28
|
--
|
%
|
ISO 4589-2 |
UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
RTI Str | UL 746 | |||
0.400 mm
|
65.0
|
--
|
°C
|
|
0.710 mm
|
85.0
|
--
|
°C
|
|
1.50 mm
|
85.0
|
--
|
°C
|
|
3.00 mm
|
85.0
|
--
|
°C
|
|
6.00 mm
|
85.0
|
--
|
°C
|
|
RTI Imp | UL 746 | |||
0.400 mm
|
65.0
|
--
|
°C
|
|
0.710 mm
|
75.0
|
--
|
°C
|
|
1.50 mm
|
75.0
|
--
|
°C
|
|
3.00 mm
|
75.0
|
--
|
°C
|
|
6.00 mm
|
75.0
|
--
|
°C
|
|
RTI Elec | UL 746 | |||
0.400 mm
|
65.0
|
--
|
°C
|
|
0.710 mm
|
130
|
--
|
°C
|
|
1.50 mm
|
130
|
--
|
°C
|
|
3.00 mm
|
130
|
--
|
°C
|
|
6.00 mm
|
130
|
--
|
°C
|
|
Comparative Tracking Index (CTI) (3.00 mm) |
> 600
|
--
|
V
|
UL 746 |
Comparative Tracking Index (CTI) (PLC) (3.00 mm) |
PLC 0
|
--
|
|
UL 746 |