| * 厂家（产地）： | 美国杜邦 | * 牌号： | 103FHS |
| * 销售方式： | 品牌经销 | 备注说明： | 原厂正牌，货到付款 |
| * 地区： | 全国 |
美国杜邦PA66 103FHS/NC010/BKB038 原厂原包，货真价实，价格优惠，亲！~
本公司长期供应透明尼龙，改性尼龙，食品级尼龙，阻燃尼龙，防火（UL94V0、5VA级）尼龙，耐磨尼龙，超韧性尼龙，耐寒耐低温尼龙，耐酸碱尼龙，抗紫外线尼龙，防水解尼龙，抗水解尼龙，增强尼龙，不吸水尼龙，无卤尼龙，热稳定尼龙，弹性尼龙，硬尼龙，挤出尼龙，注塑尼龙，等塑胶原料。
美国杜邦PA66 103FHS/NC010/BKB038物性表
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Specific Gravity |
1.14
|
--
|
g/cm³
|
ASTM D792 |
| Density |
1.14
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | |||
|
1.60 mm
|
1.4
|
--
|
%
|
|
|
3.20 mm
|
1.8
|
--
|
%
|
|
| Molding Shrinkage | ISO 294-4 | |||
|
Across Flow: 2.00 mm
|
1.3
|
--
|
%
|
|
|
Flow: 2.00 mm
|
1.4
|
--
|
%
|
|
| Water Absorption (23°C, 24 hr) |
1.2
|
--
|
%
|
ASTM D570 |
| Water Absorption (Saturation, 23°C) |
8.6
|
--
|
%
|
ASTM D570 |
| Water Absorption (Saturation, 23°C) |
8.5
|
--
|
%
|
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
2.6
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
3100
|
1400
|
MPa
|
ISO 527-2 |
| Tensile Strength | ASTM D638 | |||
|
23°C
|
83.0
|
59.0
|
MPa
|
|
|
77°C
|
55.0
|
--
|
MPa
|
|
|
121°C
|
41.0
|
--
|
MPa
|
|
| Tensile Stress (Yield, 23°C) |
85.0
|
55.0
|
MPa
|
ISO 527-2 |
| Tensile Strain (Yield, 23°C) |
4.5
|
25
|
%
|
ISO 527-2 |
| Tensile Elongation | ASTM D638 | |||
|
Break, 23°C
|
50
|
> 250
|
%
|
|
|
Break, 77°C
|
190
|
--
|
%
|
|
|
Break, 121°C
|
> 250
|
--
|
%
|
|
| Nominal Tensile Strain at Break (23°C) |
20
|
> 100
|
%
|
ISO 527-2 |
| Flexural Modulus | ASTM D790 | |||
|
23°C
|
2830
|
1210
|
MPa
|
|
|
77°C
|
1100
|
565
|
MPa
|
|
|
121°C
|
538
|
415
|
MPa
|
|
|
130°C
|
414
|
--
|
MPa
|
|
| Flexural Modulus (23°C) |
2800
|
1300
|
MPa
|
ISO 178 |
| Shear Strength (23°C) |
73.8
|
65.0
|
MPa
|
ASTM D732 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-40°C
|
3.0
|
--
|
kJ/m²
|
|
|
-30°C
|
4.5
|
3.0
|
kJ/m²
|
|
|
23°C
|
5.5
|
11
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
350 kJ/m²
|
No Break
|
|
|
|
23°C
|
No Break
|
No Break
|
|
|
| Notched Izod Impact | ASTM D256 | |||
|
23°C
|
53
|
80
|
J/m
|
|
|
77°C
|
130
|
190
|
J/m
|
|
| Notched Izod Impact Strength | ISO 180/1A | |||
|
-40°C
|
5.5
|
--
|
kJ/m²
|
|
|
-30°C
|
6.0
|
5.0
|
kJ/m²
|
|
|
23°C
|
5.5
|
11
|
kJ/m²
|
|
| Unnotched Izod Impact Strength | ISO 180/1U | |||
|
-30°C
|
300 kJ/m²
|
No Break
|
|
|
|
23°C
|
300 kJ/m²
|
No Break
|
|
|
| Tensile Impact Strength 2 | ASTM D1822 | |||
|
23°C
|
440
|
--
|
kJ/m²
|
|
|
121°C
|
510 kJ/m²
|
No Break
|
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Rockwell Hardness (R-Scale) |
121
|
--
|
|
ASTM D785 |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) |
210
|
--
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
200
|
--
|
°C
|
ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) |
65.0
|
--
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
70.0
|
--
|
°C
|
ISO 75-2/A |
| Glass Transition Temperature |
60.0
|
--
|
°C
|
ISO 11357-2 |
| Melting Temperature |
263
|
--
|
°C
|
ASTM D3418 |
| Melting Temperature 3 |
262
|
--
|
°C
|
ISO 11357-3 |
| CLTE - Flow (23 to 55°C) |
0.00010
|
--
|
cm/cm/°C
|
ASTM E831 |
| CLTE - Flow (23 to 55°C) |
0.00010
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| CLTE - Transverse (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ASTM E831 |
| CLTE - Transverse (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Volume Resistivity (23°C) |
1.0E+14
|
1.0E+11
|
ohm·cm
|
ASTM D257 |
| Volume Resistivity |
1.0E+14
|
1.0E+11
|
ohm·cm
|
IEC 60093 |
| Dielectric Constant | ASTM D150 | |||
|
23°C, 100 Hz
|
3.40
|
7.00
|
|
|
|
23°C, 1 kHz
|
3.40
|
5.60
|
|
|
|
23°C, 1 MHz
|
3.20
|
3.60
|
|
|
| Dissipation Factor | ASTM D150 | |||
|
23°C, 100 Hz
|
0.010
|
0.20
|
|
|
|
23°C, 1 kHz
|
0.010
|
0.15
|
|
|
|
23°C, 1 MHz
|
0.020
|
0.060
|
|
|
| Comparative Tracking Index |
600
|
--
|
V
|
IEC 60112 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
0.710 mm
|
V-2
|
--
|
|
|
|
1.50 mm
|
V-2
|
--
|
|
|
|
3.00 mm
|
V-2
|
--
|
|
|
| Flammability Classification | IEC 60695-11-10, -20 | |||
|
0.710 mm
|
V-2
|
--
|
|
|
|
1.50 mm
|
V-2
|
--
|
|
|
|
3.00 mm
|
V-2
|
--
|
|
|
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
|
0.710 mm
|
850
|
--
|
°C
|
|
|
1.50 mm
|
960
|
--
|
°C
|
|
|
3.00 mm
|
960
|
--
|
°C
|
|
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
|
0.710 mm
|
725
|
--
|
°C
|
|
|
1.50 mm
|
725
|
--
|
°C
|
|
|
3.00 mm
|
725
|
--
|
°C
|
|
| Oxygen Index |
28
|
--
|
%
|
ISO 4589-2 |
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
0.710 mm
|
115
|
--
|
°C
|
|
|
1.50 mm
|
125
|
--
|
°C
|
|
|
3.00 mm
|
125
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
0.710 mm
|
95.0
|
--
|
°C
|
|
|
1.50 mm
|
110
|
--
|
°C
|
|
|
3.00 mm
|
110
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.710 mm
|
140
|
--
|
°C
|
|
|
1.50 mm
|
140
|
--
|
°C
|
|
|
3.00 mm
|
140
|
--
|
°C
|
|
| Comparative Tracking Index (CTI) (3.00 mm) |
600
|
--
|
V
|
UL 746 |
| Comparative Tracking Index (CTI) (PLC) (3.00 mm) |
PLC 0
|
--
|
|
UL 746 |