* 厂家(产地): | 美国杜邦 | * 牌号: | 158L |
* 销售方式: | 品牌经销 | 备注说明: | 原厂正牌,货到付款 |
* 地区: | 全国 |
美国杜邦158L NC010 原厂原包,货真价实,价格优惠,亲!~
本公司长期供应透明尼龙,改性尼龙,食品级尼龙,阻燃尼龙,防火(UL94V0、5VA级)尼龙,耐磨尼龙,超韧性尼龙,耐寒耐低温尼龙,耐酸碱尼龙,抗紫外线尼龙,防水解尼龙,抗水解尼龙,增强尼龙,不吸水尼龙,无卤尼龙,热稳定尼龙,弹性尼龙,硬尼龙,挤出尼龙,注塑尼龙,等塑胶原料。
美国杜邦158L NC010 物性表
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Specific Gravity |
1.06
|
--
|
g/cm³
|
ASTM D792 |
Density |
1.06
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage - Flow (3.20 mm) |
1.1
|
--
|
%
|
Internal Method |
Molding Shrinkage | ISO 294-4 | |||
Across Flow: 2.00 mm
|
1.4
|
--
|
%
|
|
Flow: 2.00 mm
|
1.3
|
--
|
%
|
|
Water Absorption (23°C, 24 hr) |
0.25
|
--
|
%
|
ASTM D570 |
Water Absorption (Saturation, 23°C) |
3.0
|
--
|
%
|
ASTM D570 |
Water Absorption (Equilibrium, 23°C, 50% RH) |
1.3
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C) |
2400
|
1500
|
MPa
|
ISO 527-2 |
Tensile Strength | ASTM D638 | |||
-40°C
|
93.0
|
93.0
|
MPa
|
|
23°C
|
61.0
|
52.0
|
MPa
|
|
77°C
|
41.0
|
37.0
|
MPa
|
|
121°C
|
--
|
30.0
|
MPa
|
|
Tensile Strength | ASTM D638 | |||
Yield, -40°C
|
94.0
|
93.0
|
MPa
|
|
Yield, 23°C
|
61.0
|
51.0
|
MPa
|
|
Yield, 77°C
|
30.0
|
35.0
|
MPa
|
|
Yield, 121°C
|
--
|
17.0
|
MPa
|
|
Tensile Stress (Yield, 23°C) |
62.0
|
52.0
|
MPa
|
ISO 527-2 |
Tensile Elongation | ASTM D638 | |||
Yield, -40°C
|
8.0
|
14
|
%
|
|
Yield, 23°C
|
7.0
|
40
|
%
|
|
Yield, 77°C
|
30
|
--
|
%
|
|
Tensile Strain (Yield, 23°C) |
4.5
|
19
|
%
|
ISO 527-2 |
Tensile Elongation | ASTM D638 | |||
Break, -40°C
|
15
|
30
|
%
|
|
Break, 23°C
|
150
|
> 300
|
%
|
|
Break, 77°C
|
> 300
|
> 300
|
%
|
|
Break, 121°C
|
--
|
250
|
%
|
|
Nominal Tensile Strain at Break (23°C) |
35
|
> 100
|
%
|
ISO 527-2 |
Flexural Modulus | ASTM D790 | |||
-40°C
|
2340
|
2760
|
MPa
|
|
23°C
|
2030
|
1240
|
MPa
|
|
77°C
|
415
|
380
|
MPa
|
|
121°C
|
330
|
300
|
MPa
|
|
Flexural Modulus (23°C) |
2050
|
1450
|
MPa
|
ISO 178 |
Shear Strength (23°C) |
59.0
|
56.0
|
MPa
|
ASTM D732 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C
|
5.0
|
4.0
|
kJ/m²
|
|
23°C
|
4.0
|
6.0
|
kJ/m²
|
|
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C
|
No Break
|
--
|
|
|
23°C
|
No Break
|
No Break
|
|
|
Notched Izod Impact | ASTM D256 | |||
-40°C
|
48
|
32
|
J/m
|
|
23°C
|
53
|
75
|
J/m
|
|
Notched Izod Impact Strength | ISO 180/1A | |||
-30°C
|
5.0
|
4.0
|
kJ/m²
|
|
23°C
|
4.0
|
6.0
|
kJ/m²
|
|
Tensile Impact Strength | ASTM D1822 | |||
23°C 2
|
611
|
945
|
kJ/m²
|
|
23°C 3
|
154
|
219
|
kJ/m²
|
|
Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Rockwell Hardness (R-Scale) |
114
|
108
|
|
ASTM D785 |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature (0.45 MPa, Unannealed) |
135
|
--
|
°C
|
ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed) |
55.0
|
--
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed) |
62.0
|
--
|
°C
|
ISO 75-2/A |
Brittleness Temperature |
-126
|
-109
|
°C
|
ASTM D746 |
Melting Temperature |
218
|
--
|
°C
|
ASTM D3418 |
Melting Temperature 4 |
218
|
--
|
°C
|
ISO 11357-3 |
CLTE - Flow | ISO 11359-2 | |||
-40 to 23°C
|
0.000090
|
--
|
cm/cm/°C
|
|
-30 to 30°C
|
0.000090
|
--
|
cm/cm/°C
|
|
23 to 55°C
|
0.00012
|
--
|
cm/cm/°C
|
|
55 to 160°C
|
0.00017
|
--
|
cm/cm/°C
|
|
CLTE - Transverse | ISO 11359-2 | |||
-40 to 23°C
|
0.000090
|
--
|
cm/cm/°C
|
|
23 to 55°C
|
0.00012
|
--
|
cm/cm/°C
|
|
55 to 160°C
|
0.00018
|
--
|
cm/cm/°C
|
|
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity (23°C) |
1.0E+15
|
1.0E+13
|
ohm·cm
|
ASTM D257 |
Dielectric Constant | ASTM D150 | |||
23°C, 100 Hz
|
4.00
|
6.00
|
|
|
23°C, 1 kHz
|
4.00
|
5.30
|
|
|
23°C, 1 MHz
|
3.50
|
4.00
|
|
|
Relative Permittivity | IEC 60250 | |||
23°C, 100 Hz
|
3.60
|
--
|
|
|
23°C, 1 MHz
|
3.20
|
--
|
|
|
Dissipation Factor | ASTM D150 | |||
23°C, 100 Hz
|
0.020
|
0.15
|
|
|
23°C, 1 kHz
|
0.020
|
0.15
|
|
|
23°C, 1 MHz
|
0.020
|
0.10
|
|
|
Dissipation Factor | IEC 60250 | |||
23°C, 100 Hz
|
0.014
|
--
|
|
|
23°C, 1 MHz
|
0.016
|
--
|
|
|
Comparative Tracking Index |
600
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating - UL | UL 94 | |||
0.860 mm
|
HB
|
--
|
|
|
1.50 mm
|
HB
|
--
|
|
|
3.00 mm
|
HB
|
--
|
|
|
Flammability Classification | IEC 60695-11-10, -20 | |||
0.860 mm
|
HB
|
--
|
|
|
1.50 mm
|
HB
|
--
|
|
|
3.00 mm
|
HB
|
--
|
|
|
Oxygen Index |
25
|
28
|
%
|
ASTM D2863 |
Oxygen Index |
25
|
--
|
%
|
ISO 4589-2 |
UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
RTI Str | UL 746 | |||
0.860 mm
|
65.0
|
--
|
°C
|
|
1.50 mm
|
65.0
|
--
|
°C
|
|
3.00 mm
|
65.0
|
--
|
°C
|
|
RTI Imp | UL 746 | |||
0.860 mm
|
65.0
|
--
|
°C
|
|
1.50 mm
|
65.0
|
--
|
°C
|
|
3.00 mm
|
65.0
|
--
|
°C
|
|
RTI Elec | UL 746 | |||
0.860 mm
|
105
|
--
|
°C
|
|
1.50 mm
|
105
|
--
|
°C
|
|
3.00 mm
|
105
|
--
|
°C
|
|
Comparative Tracking Index (CTI) |
> 600
|
--
|
V
|
UL 746 |