| * 厂家（产地）： | 美国杜邦 | * 牌号： | 70G25HSLR NC010 |
| * 销售方式： | 品牌经销 | 备注说明： | 原厂正牌，货到付款 |
| * 地区： | 全国 |
Zytel 70G25HSLR NC010原厂原包，货真价实，价格优惠，亲！~
本公司长期供应透明尼龙，改性尼龙，食品级尼龙，阻燃尼龙，防火（UL94V0、5VA级）尼龙，耐磨尼龙，超韧性尼龙，耐寒耐低温尼龙，耐酸碱尼龙，抗紫外线尼龙，防水解尼龙，抗水解尼龙，玻纤增强,增强尼龙，不吸水尼龙，无卤尼龙，热稳定尼龙，弹性尼龙，硬尼龙，挤出尼龙，注塑尼龙，等塑胶原料。
Zytel 70G25HSLR NC010物性表
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Density |
1.32
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
|
Across Flow: 2.00 mm
|
1.1
|
--
|
%
|
|
|
Flow: 2.00 mm
|
0.30
|
--
|
%
|
|
| Water Absorption (Saturation, 23°C) |
6.4
|
--
|
%
|
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
2.0
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
8400
|
6100
|
MPa
|
ISO 527-2 |
| Tensile Stress (Break, 23°C) |
180
|
120
|
MPa
|
ISO 527-2 |
| Tensile Strain (Break, 23°C) |
3.0
|
7.0
|
%
|
ISO 527-2 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-30°C
|
7.0
|
7.0
|
kJ/m²
|
|
|
23°C
|
10
|
11
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
60
|
45
|
kJ/m²
|
|
|
23°C
|
60
|
80
|
kJ/m²
|
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
261
|
--
|
°C
|
ISO 75-2/B |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
252
|
--
|
°C
|
ISO 75-2/A |
| Glass Transition Temperature |
80.0
|
--
|
°C
|
ISO 11357-2 |
| Melting Temperature 2 |
262
|
--
|
°C
|
ISO 11357-3 |
| CLTE - Flow (23 to 55°C) |
0.000033
|
--
|
cm/cm/°C
|
ASTM E831 |
| CLTE - Flow (23 to 55°C) |
0.000033
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| CLTE - Transverse (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ASTM E831 |
| CLTE - Transverse (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Surface Resistivity |
--
|
1.0E+13
|
ohms
|
IEC 60093 |
| Volume Resistivity |
1.0E+15
|
--
|
ohm·cm
|
IEC 60093 |
| Relative Permittivity (23°C, 100 Hz) |
3.60
|
--
|
|
IEC 60250 |
| Dissipation Factor (23°C, 100 Hz) |
0.0070
|
--
|
|
IEC 60250 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
1.50 mm
|
HB
|
--
|
|
|
|
3.00 mm
|
HB
|
--
|
|
|
| Flammability Classification | IEC 60695-11-10, -20 | |||
|
1.50 mm
|
HB
|
--
|
|
|
|
3.00 mm
|
HB
|
--
|
|
|
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
1.50 mm
|
105
|
--
|
°C
|
|
|
3.00 mm
|
110
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
1.50 mm
|
95.0
|
--
|
°C
|
|
|
3.00 mm
|
95.0
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.710 mm
|
105
|
--
|
°C
|
|
|
1.50 mm
|
120
|
--
|
°C
|
|
|
3.00 mm
|
120
|
--
|
°C
|