* 厂家(产地): | 美国杜邦 | * 牌号: | 70G30HSL NC010 |
* 销售方式: | 品牌经销 | 备注说明: | 原厂正牌,货到付款 |
* 地区: | 全国 |
本公司长期供应透明尼龙,改性尼龙,食品级尼龙,阻燃尼龙,防火(UL94V0、5VA级)尼龙,耐磨尼龙,超韧性尼龙,耐寒耐低温尼龙,耐酸碱尼龙,抗紫外线尼龙,防水解尼龙,抗水解尼龙,玻纤增强,增强尼龙,不吸水尼龙,无卤尼龙,热稳定尼龙,弹性尼龙,硬尼龙,挤出尼龙,注塑尼龙,等塑胶原料。
Zytel 70G30HSL NC010英文物性表
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density |
1.37
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow: 2.00 mm
|
1.1
|
--
|
%
|
|
Flow: 2.00 mm
|
0.30
|
--
|
%
|
|
Water Absorption (Saturation, 23°C) |
6.0
|
--
|
%
|
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) |
1.9
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C) |
10000
|
7200
|
MPa
|
ISO 527-2 |
Tensile Stress (Break, 23°C) |
195
|
125
|
MPa
|
ISO 527-2 |
Tensile Strain (Break, 23°C) |
3.4
|
5.0
|
%
|
ISO 527-2 |
Tensile Creep Modulus (1 hr) |
--
|
6800
|
MPa
|
ISO 899-1 |
Tensile Creep Modulus (1000 hr) |
--
|
5100
|
MPa
|
ISO 899-1 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C
|
10
|
10
|
kJ/m²
|
|
23°C
|
12
|
16
|
kJ/m²
|
|
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C
|
70
|
73
|
kJ/m²
|
|
23°C
|
82
|
93
|
kJ/m²
|
|
Notched Izod Impact Strength (23°C) |
13
|
17
|
kJ/m²
|
ISO 180/1A |
Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Rockwell Hardness | ISO 2039-2 | |||
M-Scale
|
104
|
88
|
|
|
R-Scale
|
124
|
117
|
|
|
Ball Indentation Hardness (H 961/30) |
275
|
187
|
MPa
|
ISO 2039-1 |
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature (0.45 MPa, Unannealed) |
261
|
--
|
°C
|
ISO 75-2/Bf |
Heat Deflection Temperature (1.8 MPa, Unannealed) |
248
|
--
|
°C
|
ISO 75-2/Af |
Vicat Softening Temperature |
250
|
--
|
°C
|
ISO 306/B |
Melting Temperature (DSC) |
263
|
--
|
°C
|
ISO 3146 |
CLTE - Flow (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse (23 to 55°C) |
0.000022
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Surface Resistivity |
1.0E+15
|
1.0E+13
|
ohms
|
IEC 60093 |
Volume Resistivity |
1.0E+17
|
1.0E+11
|
ohm·cm
|
IEC 60093 |
Relative Permittivity | IEC 60250 | |||
100 Hz
|
4.40
|
10.8
|
|
|
1 MHz
|
4.10
|
4.60
|
|
|
Dissipation Factor | IEC 60250 | |||
100 Hz
|
0.0070
|
0.46
|
|
|
1 MHz
|
0.015
|
0.065
|
|
|
Comparative Tracking Index |
400
|
--
|
V
|
IEC 60112 |
Electric Strength (1.00 mm) |
38
|
32
|
kV/mm
|
IEC 60243-1 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating - UL | UL 94 | |||
0.750 mm
|
HB
|
--
|
|
|
1.50 mm
|
HB
|
--
|
|
|
3.00 mm
|
HB
|
--
|
|
|
Flammability Classification | IEC 60695-11-10, -20 | |||
0.750 mm
|
HB
|
--
|
|
|
1.50 mm
|
HB
|
--
|
|
|
3.00 mm
|
HB
|
--
|
|
|
UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
RTI Str | UL 746 | |||
0.750 mm
|
140
|
--
|
°C
|
|
1.50 mm
|
140
|
--
|
°C
|
|
3.00 mm
|
140
|
--
|
°C
|
|
RTI Imp | UL 746 | |||
0.750 mm
|
125
|
--
|
°C
|
|
1.50 mm
|
125
|
--
|
°C
|
|
3.00 mm
|
125
|
--
|
°C
|
|
RTI Elec | UL 746 | |||
0.750 mm
|
140
|
--
|
°C
|
|
1.50 mm
|
140
|
--
|
°C
|
|
3.00 mm
|
140
|
--
|
°C
|
|
Comparative Tracking Index (CTI) (3.00 mm) |
400
|
--
|
V
|
UL 746 |
Hot-wire Ignition (HWI) | UL 746 | |||
0.750 mm
|
7.0
|
--
|
sec
|
|
1.50 mm
|
7.0
|
--
|
sec
|
|
3.00 mm
|
60
|
--
|
sec
|
|
High Amp Arc Ignition (HAI) | UL 746 | |||
0.750 mm
|
120
|
--
|
|
|
1.50 mm
|
120
|
--
|
|
|
3.00 mm
|
120
|
--
|
|