Zytel 70G30HSL BK031英文物性表
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Density |
1.37
|
--
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
|
Across Flow: 2.00 mm
|
1.1
|
--
|
%
|
|
|
Flow: 2.00 mm
|
0.30
|
--
|
%
|
|
| Water Absorption (Saturation, 23°C) |
6.0
|
--
|
%
|
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
1.9
|
--
|
%
|
ISO 62 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
10000
|
7200
|
MPa
|
ISO 527-2 |
| Tensile Stress (Break, 23°C) |
195
|
125
|
MPa
|
ISO 527-2 |
| Tensile Strain (Break, 23°C) |
3.4
|
5.0
|
%
|
ISO 527-2 |
| Tensile Creep Modulus (1 hr) |
--
|
6800
|
MPa
|
ISO 899-1 |
| Tensile Creep Modulus (1000 hr) |
--
|
5100
|
MPa
|
ISO 899-1 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
|
-30°C
|
10
|
10
|
kJ/m²
|
|
|
23°C
|
12
|
16
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
|
-30°C
|
70
|
73
|
kJ/m²
|
|
|
23°C
|
82
|
93
|
kJ/m²
|
|
| Notched Izod Impact Strength (23°C) |
13
|
17
|
kJ/m²
|
ISO 180/1A |
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Rockwell Hardness | ISO 2039-2 | |||
|
M-Scale
|
104
|
88
|
|
|
|
R-Scale
|
124
|
117
|
|
|
| Ball Indentation Hardness (H 961/30) |
275
|
187
|
MPa
|
ISO 2039-1 |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
261
|
--
|
°C
|
ISO 75-2/Bf |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
248
|
--
|
°C
|
ISO 75-2/Af |
| Vicat Softening Temperature |
250
|
--
|
°C
|
ISO 306/B |
| Melting Temperature (DSC) |
263
|
--
|
°C
|
ISO 3146 |
| CLTE - Flow (23 to 55°C) |
0.00011
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| CLTE - Transverse (23 to 55°C) |
0.000022
|
--
|
cm/cm/°C
|
ISO 11359-2 |
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Surface Resistivity |
1.0E+15
|
1.0E+13
|
ohms
|
IEC 60093 |
| Volume Resistivity |
1.0E+17
|
1.0E+11
|
ohm·cm
|
IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
|
100 Hz
|
4.40
|
10.8
|
|
|
|
1 MHz
|
4.10
|
4.60
|
|
|
| Dissipation Factor | IEC 60250 | |||
|
100 Hz
|
0.0070
|
0.46
|
|
|
|
1 MHz
|
0.015
|
0.065
|
|
|
| Comparative Tracking Index |
400
|
--
|
V
|
IEC 60112 |
| Electric Strength (1.00 mm) |
38
|
32
|
kV/mm
|
IEC 60243-1 |
| Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | |||
|
0.750 mm
|
HB
|
--
|
|
|
|
1.50 mm
|
HB
|
--
|
|
|
|
3.00 mm
|
HB
|
--
|
|
|
| Flammability Classification | IEC 60695-11-10, -20 | |||
|
0.750 mm
|
HB
|
--
|
|
|
|
1.50 mm
|
HB
|
--
|
|
|
|
3.00 mm
|
HB
|
--
|
|
|
| UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| RTI Str | UL 746 | |||
|
0.750 mm
|
140
|
--
|
°C
|
|
|
1.50 mm
|
140
|
--
|
°C
|
|
|
3.00 mm
|
140
|
--
|
°C
|
|
| RTI Imp | UL 746 | |||
|
0.750 mm
|
125
|
--
|
°C
|
|
|
1.50 mm
|
125
|
--
|
°C
|
|
|
3.00 mm
|
125
|
--
|
°C
|
|
| RTI Elec | UL 746 | |||
|
0.750 mm
|
140
|
--
|
°C
|
|
|
1.50 mm
|
140
|
--
|
°C
|
|
|
3.00 mm
|
140
|
--
|
°C
|
|
| Comparative Tracking Index (CTI) (3.00 mm) |
400
|
--
|
V
|
UL 746 |
| Hot-wire Ignition (HWI) | UL 746 | |||
|
0.750 mm
|
7.0
|
--
|
sec
|
|
|
1.50 mm
|
7.0
|
--
|
sec
|
|
|
3.00 mm
|
60
|
--
|
sec
|
|
| High Amp Arc Ignition (HAI) | UL 746 | |||
|
0.750 mm
|
120
|
--
|
|
|
|
1.50 mm
|
120
|
--
|
|
|
|
3.00 mm
|
120
|
--
|
|